| 1. Identificação | |
| Tipo de Referência | Artigo em Revista Científica (Journal Article) |
| Site | mtc-m21b.sid.inpe.br |
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
| Identificador | 8JMKD3MGP5W34M/3HE6T34 |
| Repositório | sid.inpe.br/mtc-m21b/2014/11.19.02.19.32 (acesso restrito) |
| Última Atualização | 2015:02.11.15.01.47 (UTC) administrator |
| Repositório de Metadados | sid.inpe.br/mtc-m21b/2014/11.19.02.19.33 |
| Última Atualização dos Metadados | 2018:06.04.03.04.36 (UTC) administrator |
| DOI | 10.1016/j.apsusc.2014.04.142 |
| ISSN | 0169-4332 |
| Rótulo | isi 2014-11 FernandesMandOlivUeda:2014:MePrNi |
| Chave de Citação | FernandesMandOlivUeda:2014:MePrNi |
| Título | Mechanical properties of nitrogen-rich surface layers on SS304 treated by plasma immersion ion implantation  |
| Ano | 2014 |
| Mês | Aug. |
| Data de Acesso | 21 maio 2024 |
| Tipo de Trabalho | journal article |
| Tipo Secundário | PRE PI |
| Número de Arquivos | 1 |
| Tamanho | 4950 KiB |
| 2. Contextualização | |
| Autor | 1 Fernandes, Bruno Bacci 2 Mandl, S. 3 Oliveira, Rogerio de Moraes 4 Ueda, Mario |
| Identificador de Curriculo | 1 2 3 8JMKD3MGP5W/3C9JJ6L 4 8JMKD3MGP5W/3C9JHSB |
| Grupo | 1 LAP-CTE-INPE-MCTI-GOV-BR 2 3 LAP-CTE-INPE-MCTI-GOV-BR 4 LAP-CTE-INPE-MCTI-GOV-BR |
| Afiliação | 1 Instituto Nacional de Pesquisas Espaciais (INPE) 2 Leibniz Inst Oberflachenmodifizierung 3 Instituto Nacional de Pesquisas Espaciais (INPE) 4 Instituto Nacional de Pesquisas Espaciais (INPE) |
| Endereço de e-Mail do Autor | 1 bruno.bacci@plasma.inpe.br 2 3 rogerio@plasma.inpe.br 4 ueda@plasma.inpe.br |
| Endereço de e-Mail | marcelo.pazos@inpe.br |
| Revista | Applied Surface Science |
| Volume | 310 |
| Número | SI |
| Páginas | 278-283 |
| Nota Secundária | A1_ENGENHARIAS_II A1_ENGENHARIAS_I A1_INTERDISCIPLINAR A2_ENGENHARIAS_III A2_CIÊNCIAS_AGRÁRIAS_I A2_MATERIAIS A2_SAÚDE_COLETIVA B1_GEOCIÊNCIAS B1_ODONTOLOGIA B1_QUÍMICA B1_CIÊNCIAS_BIOLÓGICAS_I B1_ENGENHARIAS_IV B1_MATEMÁTICA_/_PROBABILIDADE_E B1_MEDICINA_II B1_MEDICINA_III B1_FARMÁCIA B1_BIOTECNOLOGIA B2_ENSINO B2_ASTRONOMIA_/_FÍSICA B2_CIÊNCIAS_BIOLÓGICAS_II C_BIODIVERSIDADE |
| Histórico (UTC) | 2018-06-04 03:04:36 :: administrator -> marcelo.pazos@inpe.br :: 2014 |
| 3. Conteúdo e estrutura | |
| É a matriz ou uma cópia? | é a matriz |
| Estágio do Conteúdo | concluido |
| Transferível | 1 |
| Tipo do Conteúdo | External Contribution |
| Tipo de Versão | publisher |
| Palavras-Chave | Stainless steel Plasma immersion ion implantation Tribological properties Hardness |
| Resumo | The formation of hard and wear resistant surface regions for austenitic stainless steel through different nitriding and nitrogen implantation processes at intermediate temperatures is an established technology. As the inserted nitrogen remains in solid solution, an expanded austenite phase is formed, accounting for these surface improvements. However, experiments on long-term behavior and exact wear processes within the expanded austenite layer are still missing. Here, the modified layers were produced using plasma immersion ion implantation with nitrogen gas and had a thickness of up to 4 pm, depending on the processing temperature. Thicker layers or those with higher surface nitrogen contents presented better wear resistance, according to detailed microscopic investigation on abrasion, plastic deformation, cracking and redeposition of material inside the wear tracks. At the same time, cyclic fatigue testing employing a nanoindenter equipped with a diamond ball was carried out at different absolute loads and relative unloadings. As the stress distribution between the modified layer and the substrate changes with increasing load, additional simulations were performed for obtaining these complex stress distributions. While high nitrogen concentration and/or thicker layers improve the wear resistance and hardness, these modifications simultaneously reduce the surface fatigue resistance. |
| Área | FISPLASMA |
| Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAP > Mechanical properties of... |
| Conteúdo da Pasta doc | acessar |
| Conteúdo da Pasta source | não têm arquivos |
| Conteúdo da Pasta agreement | não têm arquivos |
| 4. Condições de acesso e uso | |
| Idioma | en |
| Arquivo Alvo | Fernandes_Mechanical.pdf |
| Grupo de Usuários | administrator marcelo.pazos@inpe.br |
| Grupo de Leitores | administrator marcelo.pazos@inpe.br |
| Visibilidade | shown |
| Política de Arquivamento | denypublisher denyfinaldraft24 |
| Permissão de Leitura | deny from all and allow from 150.163 |
| Permissão de Atualização | não transferida |
| 5. Fontes relacionadas | |
| Vinculação | Trabalho não Vinculado à Tese/Dissertação |
| Repositório Espelho | iconet.com.br/banon/2006/11.26.21.31 |
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ET2RFS |
| Lista de Itens Citando | sid.inpe.br/mtc-m21/2012/07.13.14.59.24 3 sid.inpe.br/bibdigital/2013/09.25.21.49 2 sid.inpe.br/mtc-m21/2012/07.13.14.56.06 1 |
| Divulgação | WEBSCI; PORTALCAPES; COMPENDEX; SCOPUS. |
| Acervo Hospedeiro | sid.inpe.br/mtc-m21b/2013/09.26.14.25.20 |
| 6. Notas | |
| Campos Vazios | alternatejournal archivist callnumber copyholder copyright creatorhistory descriptionlevel format isbn lineage mark nextedition notes orcid parameterlist parentrepositories previousedition previouslowerunit progress project rightsholder schedulinginformation secondarydate secondarykey session shorttitle sponsor subject tertiarytype url |
| 7. Controle da descrição | |
| e-Mail (login) | marcelo.pazos@inpe.br |
| atualizar | |